Much effort has been invested into research on developing catalysts on low temperature polymer electrolyte fuel cell over the last two decades.  Platinum metal is a widely used material for these catalysts, but due to high cost and insufficient availability, new catalysts are being developed.  In an effort to reduce the platinum group metal (PGM) loading for the cathode in hydrogen-air fuel cells, JPL has examined a wide range of alloy compositions where Pt metal is alloyed with valve metals (Ti, V, and Zr) and the late transition metals (Co, Ni).  The results of the electrochemical measurements, voltage swept cyclic voltammograms and potentiodynamic polarization curves, were investigated using the rotating disk electrode (RDE), and the novel multi-electrode electrochemical test system developed at JPL.  The samples that were studied were PtTF, and PtCoZr.  In each system, measurements of the active area, revealed by measuring the area associated with the hydrogen-oxidation-reaction (HER) at anodic potentials were conducted; along with polarization curves conducted to determine the oxygen-reduction-reaction (ORR) current density at 0.9 V, vs. NHE).   The sample studied was an array of PtCoZr thin films, with up to 30 atomic % Zr, and as little as 56 atomic % Pt, present in the alloy. This five year old sample was measured again for its electrochemical activity.  This sample exhibited outstanding electrochemical activity in its original condition (110�A/cm^2 ORR, > 10X larger than (111) Pt thin films), and large surface areas (250�C/cm^2, ~ 2X > (111) Pt.).  Previous measurements showed reproducible results with up to one year or more between measurements. X-ray photo-electron-spectroscopy (XPS) measurements showed that the electrochemically treated surface was dominated by Pt-Zr surface layers, with Co, being leached from the surface, and/or reconstructing below the upper surface. The ozone ashing treatment used to prepare the surface for XPS measurements resulted in a 3X loss of electrochemical ORR activity, due to the formation of complex oxides at the specimen surface.  During five years of measurements, this sample underwent aggressive durability testing; e.g., thousands of cycles up to 1.6V NHE.  Regardless of the extreme conditions, this sample still shows decent ORR activity (40�A/cm^2, still > 4X larger than (111) Pt), and active areas (230�C/cm^2), comparable to polycrystalline.  From this we can conclude that this sample is still active and very durable to harsh conditions. [Acknowledgment: NASA Space Grant funded this study in collaboration with the Department of Energy at JPL-Caltech]

High-throughput electrochemical characterization of fuel cell catalysts

247th National Meeting (2014)

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.