A strategy is developed to enhance the barrier protection of polyethylene oxide (PEO)-metal organic framework (MOF) composite films against chemical warfare agent (CWA) simulants. To achieve enhanced protection, an impermeable high-aspect-ratio filler in the form of Laponite RD (LRD) clay platelets was incorporated into a composite PEO film containing the MOF UiO-66-NH2. The inclusion of the platelets aids in mitigating permeation of inert hydrocarbons (octane) and toxic chemicals (2-chloroethyl ethyl sulfide, 2-CEES) of dimensions/chemistry similar to prominent vesicant threats while still maintaining high water vapor transport rates (WVTR). By utilizing small-angle neutron scattering (SANS), small-angle x-ray scattering (SAXS) and wide-angle x-ray scattering (WAXS), the LRD platelet alignment of the films was determined and the structure of the films was correlated with performance as a barrier material. Performance of the membranes against toxic chemical threats was assessed using permeation testing of octane and 2-CEES, a common simulant for the vesicant mustard gas, and breathability of the membranes was assessed using water vapor transport rate (WVTR) measurements. To assess their robustness, chemical exposure (in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS)) and mechanical (tensile strength) measurements were also performed. It was demonstrated that the barrier performance of the film upon inclusion of the LRD platelets exceeds that of other MOF-polymer composites found in the literature and that this approach establishes a new path for improving permselective materials for chemical protection applications.

Laponite-incorporated UiO-66-NH2-polyethylene oxide composite membranes for protection against chemical warfare agent simulants

ACS Spring Meeting 2021

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.