2-phenyl-1,1-dicyanoethylenes, RC6H4CH=C(CN)2 (where R is 2-methoxy, 3-methoxy, 4-methoxy, 2-ethoxy, 3-ethoxy, 4-ethoxy, 4-propoxy, 4-buthoxy, 4-hexyloxy) and 4-fluorostyrene were prepared at equimolar monomer feed composition by solution copolymerization in the presence of a radical initiator (ABCN) at 70�C. The composition of the copolymers was calculated from nitrogen analysis, and the structures were analyzed by IR, 1H and 13C-NMR. The order of relative reactivity (1/r1) for the monomers is 2-methoxy (1.5) > 4-ethoxy (1.0) > 4-methoxy (0.8) > 3-ethoxy (0.7) = 3-methoxy (0.7) > 4-hexyloxy (0.6) = 2-ethoxy (0.6) > 4-butoxy (0.5) = 4-propoxy (0.5). High Tg of the copolymers, in comparison with that of poly(4-fluorostyrene) indicates a substantial decrease in chain mobility of the copolymer due to the high dipolar character of the trisubstituted ethylene monomer unit. Decomposition of the copolymers in nitrogen occurred in two steps, first in 183�500�C range with residue (5-30% wt.), which then decomposed in the 500-800�C range.

Novel copolymers of some ring-substituted 2-phenyl-1,1-dicyanoethylenes with 4-fluorostyrene

240th National Meeting (2010)

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.