The ability to alter surface properties such as morphology and surface energy upon external stimuli makes switchable polymer surfaces a promising field of research. Mixed polymer brushes consisting of two different homopolymers covalently attached to a surface are one system in which surface properties can be switched. In this work the correlation between the change in structure and the resulting surface stress in thin poly(methyl methacrylate)-polystyrene mixed polymer brush film upon exposure to selective solvents is investigated. By measuring the forces acting inside the film, we are able to achieve a deeper understanding of the observed structural changes. To obtain a thorough understanding of the film's morphology, the structure is analyzed by SPM, XRR and GISAXS.Upon exposure to acetic acid, a selective solvent for PMMA, the film showed a dimple like structure. This is linked to collapsed domains of polystyrene covered by PMMA chains. Bending experiments resulted in tensile stress, pointing to attractive forces acting inside the polymer film. After exposure to dichloromethane a good solvent for both polymers, bending experiments revealed a decreased but still high tensile stress, indicating that the micro domains are still present. GISAXS measurements verified the presence of microdomains at the surface, confirming the proposed reason for the measured tensile stress. The results of the experiments enable us to further explain the domain memory effect typically found in these kind of mixed polymer brush systems.

Stress-structure correlation in PS-PMMA mixed polymer brushes

243rd National Meeting (2012)

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.