We report our ongoing research on polyamide aerogels made by step growth polymerization using a combination of terephthaloyl chloride, isophthaloyl chloride and m-phenylenediamine. Crosslinking of the amine capped polymer chains with 1,3,5-benzenetricarbonyl trichloride causes gelation in as little as two to five minutes. Removing the reaction solvent is accomplished through solvent exchange, followed by drying using supercritical CO2 extraction to give colorless aerogels with densities ranging from 0.07 to 0.33 g/cm3 and surface areas as high as 440 m2/g. Statistical experimental design methodology has been utilized to investigate dependence of properties of these aerogels, such as density, compressive modulus, and surface area, on changes in fabrication parameters including formulated number of amide oligomer repeat units (n-value), acid chloride (meta, para or combination), and solids concentration of solution used for gelation. For example, the density of these materials was found to be dependent on the acid chloride type and the solids concentration, but n was not a significant variable. However, surface area was significantly influenced by all three parameters. The polyamide aerogels represent a potential cost savings over previously reported polyimide aerogels, since monomers are all inexpensive and commercially available. Surface area and density were both highest when 100 % terephthaloyl chloride was used but a combination of 5% solid concentration, 100% terephthaloyl chloride and n of 20 gave the best combination of properties. Figure 1. <img src='https://acs-archive-assets2.s3.amazonaws.com/240nm/uploads/40139_acs2010_2.jpg' alt='' />

Synthesis and properties of cross-linked polyamide aerogels

247th National Meeting (2014)

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.