Porous carbon was prepared by pyrolysis of  polybenzoxazine gel, which was synthesized through a sol-gel process, at high temperature under inert atmostphere. Further activation of CA resulted in an activated CA. The CA and activated CA have surface area of 466 m2/g and 917 m2/g with uniform mesopore radius of 2.4 nm and 2.5 nm, respectively. New gas sensing conductive polymer composites, fabricated from poly (vinyl alcohol) and polybutadiene filled with polybenzoxazine-based CA, have been investigated for organic vapor detection. The experimental results showed that high polar poly (vinyl alcohol) gave a higher response to high polar solvent, ie. water, and moderate polar solvent, ie. Acetone, but a lower response to low polar solvent, ie. n-hexane and toluene. On the other hand, the response of non-polar polybutadiene was excellent to n-hexane and toluene but not to water and acetone. Moreover, CA polymer composites showed better gas response compared to graphite polymer composites since CA is a nano-porous material, which has a high adsorption capacity. Moreover, CA polymer composites showed good reproducibility as the electrical resistance came back to the original value when they were exposed to N2 gas. This study shows that CA composite films have potential to be used as gas sensors.

Designing microstructure of porous carbon and its applications as a conductive filler for volatile gas sensor

248th National Meeting (2014)

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.