The industry widely uses steel repair sleeves to repair defects in pipes. This paper will focus on the types of repairs used for crack-like defects where there may be concerns of crack propagation in service from operating pressure cycles. The length of the repair sleeve, the pressure at the time of the repair and the absence of fillet welds (Type A sleeve) can all affect the future integrity of the repair.

Type B sleeves (fillet weld connecting the sleeve to the pipe) are widely used in the pipeline industry to repair crack-like flaws. Current standards require a minimum of two inches of sleeve material past the edge of a defect. A case study will show if this length is adequate under various operating conditions to ensure the defect does not propagate in service to extend beyond the fillet welds.

A pipe with a surface crack and the sleeve repair are modeled using finite element analysis to compute the crack front stress intensity. Contact interaction between the pipe’s outside surface and the sleeve’s inside surface provides the load path from the pipe to the sleeve. The contact interaction is varied from frictionless to fully bonded to vary the amount of crack opening permitted by the sleeve. The stress intensity is compared for each case to quantify the effect of the sleeve repair on reducing the hoop stress and reducing the crack’s stress intensity.

Operators often take a pressure reduction during an in-service repair both for safety reasons and to assist with obtaining a tight fit-up between the carrier pipe and the steel sleeve. An additional benefit of a pressure reduction can be gained in relation to in-service crack growth. A case study will show how a pressure reduction can extend the fatigue life of a resident defect.

Again, comparing the crack front stress intensity shows the effect on the crack of the pressure reduction when the sleeve is applied. Fatigue crack propagation analysis of several cases shows how the pressure reduction affects the crack growth rates. The analysis method can be used to examine trade-offs between the amount of pressure reduction on fatigue life versus operational requirements.

Lastly, results will be shown for various operating scenarios to support the use of a Type A sleeve on crack-like defects by varying parameters such as sleeve thickness, sleeve length, repair pressure, sleeve type, crack size and crack location.


Pipe Sleeve Repair Analysis Case Study Examining Axial Surface Cracks With Pressure Reduction and Geometry Factors to Improve Remaining Life

Division / Sponsors: 
Pipeline Systems Division

Paper Proceedings: https://asmedigitalcollection.asme.org/IPC/IPC2020/volume/84447

IPC2020 - Virtual Conference

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.