*Surface mount technology (SMT) is a revolutionary change in the electronics industry. It enables electronics industries to progress towards becoming smaller, lighter, denser, and cheaper components. The reliability of these components to coefficient of thermal expansion (CTE) mismatches, shock loading, and high-temperature applications becomes critical to performance parameters. Defense electronics may often be subjected to high-g acceleration loads in addition to extremes of temperature, humidity, and prolonged storage. Underfills provide excellent protection and survivability expectations under extreme thermos-mechanical loading, CTE mismatches, moisture. There is a dearth of computational tools to allow for the prediction of the initiation of damage and the progression of damage under high-g shock loads.  Defense electronics and military systems have longer lifetimes about 20-40 years and higher reliability requirements.  New packaging architectures, which often push the edge of the envelope in terms of miniaturization, cannot be compared with the state-of-art systems and lack decades of historical data to provide robust proof of their survivability.  Tools and techniques are needed to determine the failure envelopes for new component technologies for operation under high acceleration loads in current and next-generation military systems.  In this paper, the interface fracture toughness of the PCB-UF interface has been studied under exposure to high-temperature storage.  A three-point composite beam specimen has been used to study the interface fracture toughness.  The bi-material strips of PCB/Underfill were thermally aged for 10 days, 30 days, 60 days at temperatures ranging from 100°C to 150°C, and then the sample specimens were subjected to quasi-static three-point bending to observe fracture parameters and to determine interfacial delamination of bi-material strips.  A 2D Digital Image Correlation (DIC) method was also employed to understand the Crack tip opening displacement (CTOD), crack initiation and fracture toughness, CTOD were compared with the aging schedule and temperature. The experimental findings were fitted using linear regression to identify Crack opening displacement and to smooth out noise in the data set. A FE model was developed with cohesive zone parameters, where the crack opening displacements are provided as inputs to the model as a parameter of high temperature aging to predict the crack propagation, delamination behavior, and validated with experimental data.*

*Keywords: - PCB/Underfill system, three-point bend, interfacial delamination, fracture toughness, crack tip opening Displacement, 2D DIC.*


Experimental and  Fe Modelling  Study of Crack Propagation at the Pcb/underfill Interface Due to Iso-Thermal Aging

Division / Sponsors: 
Electronic & Photonic Packaging Division (EPPD)

Paper Proceedings: https://asmedigitalcollection.asme.org/InterPACK/InterPACK2020/volume/84041

InterPACK2020 - Virtual Conference

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.