Carbon Fiber Reinforced Polymers (CFRPs) have become an essential part of designing and engineering lightweight rigid bodies; predominantly in the aerospace and automotive industries. Typical epoxy-based CFRPs exhibit virtually no plasticity with minimal strain to failure. Although CFRPs have high specific strengths and elastic moduli, the brittle fracture mechanism presents unique challenges in failure detection for the Army’s vertical lift vehicles since failure occurs catastrophically. Most real-time structural health monitoring (SHM) techniques for composite aerospace structures are intrusive to the surface of the part and/or requires electrical connectivity. The Army uses a “safe-life” interval-based service methodology where components are replaced with regards to a usage spectrum rather than the component’s actual state of structural health. This paper explores a method for solving this problem by investigating the possibility of embedding Terfenol-D particles (\~100 microns in diameter), a magnetostrictive material, into the CFRPs for embedded non-contact, real-time, structural health monitoring. For baseline results, the change in localized (32 mm^2^ field of view) magnetic flux was only 0.02% for an applied load of 0-100% of the material’s ultimate tensile strength (UTS). For quasi-static testing procedure of specimen 5714 (15 wt.% Terfenol-D embedded CFRP) on a 0-40% loading interval of the material’s UTS, there was an observed localized (32 mm^2^ field of view) magnetic flux gradient of more than 5 mT (4%) with a reversible flux of 100%. For quasi-static testing procedure of specimen 5714 (15 wt.% Terfenol-D embedded CFRP) on a 0-70% loading interval of the material’s UTS, there was an observed localized (32 mm^2^ field of view) magnetic flux gradient of more than 3 mT (2%) with a reversible flux of only 25%. Terfenol-D embedded CRFPs have shown promising results for detecting instantaneous levels of degradation. Acoustic emission (AE), X-ray computed tomography (CT) scanning were used to validate the observed results.


Terfenol-D Carbon Fiber Reinforced Polymer (CFRP) Embedded Sensing for Early Localized Damage Detection

Division / Sponsors: 
Aerospace Division

Paper Proceedings: https://asmedigitalcollection.asme.org/SMASIS/SMASIS2020/volume/84027

SMASIS2020 - Virtual Conference

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.