<p>The indications of a high quantity of cracks from non-destructive testing measurements were determined in a root cause analysis as hydrogen flakes positioned in segregated zones in the base material of pressure vessels of Belgian nuclear power plants. Because of the laminar and quasi-laminar orientations of this hydrogen flakes with an inclination up to 16° to the pressure retaining surface the crack tips undergo predominantly mixed-mode loading conditions under internal pressure and the induced stress and strain fields of the single crack tips influence each other. In a former paper, the failure behavior of crack fields under mixed mode loading conditions was investigated at RT and -100°C, the upper shelf and the lower transition phase of the steel 22NiMoCr3-7, respectively. In this paper, the failure behavior of crack fields is investigated for many different levels of material toughness (from to upper shelf to the lower shelf region) on experiments with different artificial manufactured crack fields. Therefore, numerical simulations are carried out with extended micromechanical based damage mechanics models. For the description of ductile failure the Rousselier model is used and the Beremin model to calculate the probability of cleavage fracture. To account the sensitivity for low stress triaxiality damage by shear loading, the damage mechanics model was enhanced with a term to account for damage evolution by shear. For numerical simulations in the transition region of brittle-to-ductile failure a coupled damage mechanics model (enhanced Rousselier &amp; Beremin) will be used. In this paper, the current state of the ongoing research project is presented.</p>

Temperature Dependent Failure Behaviour of Components Containing Crack Fields: An Experimental and Numerical Approach

Paper Proceedings: https://asmedigitalcollection.asme.org/PVP/PVP2021/volume/85314

ASME 2021 Pressure Vessels & Piping Conference (PVP2021)

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.