<p>This work highlights the detrimental influence of low melting point elements such as sulfur, phosphorus, and silicon on the susceptibility of austenitic stainless steel grade 310 on pressure vessels welding joints. Defected weld seams from a vessel component were analyzed in this failure case study. Transverse linear cracks on both the circumferential and longitudinal welding seams, with excess bleeding, were revealed during the examination of the defected welding joints through Dye Penetrant Testing (DPT). The ferrite number (FN), a description of the ferrite content, was found to be less than 1.0 FN on the weld metal (WM) and 1.5 FN on the parent metal (PM). Hardness testing showed high values (295 HB max.) on the parent material PM while it was found within the range (211 HB max.) at the weld metal. The chemical composition of the WM, with the use of X- Ray Fluorescence (XRF) spectrometer, revealed 0.09% S, 0.09% P and 2.27% Si which are deemed to be in critical range against the susceptibility of SS310 to solidification cracking. The microstructure of the weld material WM displayed extensive cracking at the austenite grain boundaries of the cellular dendrites, in which film like features were observed on the crack surfaces along the interdentric interfaces. It is suggested that sulfur and phosphorus combine with iron to form low-melting compounds, which as a result can form low melting eutectics with impact to segregate at the austenitic grain boundaries during solidification. Therefore, in line with the literature, adequate control of such low melting point elements (S, P to &lt; than 0.002%, and Si away from 1.5-2.5%) was found essential to reduce the susceptibility of SS310 welding joints to hot cracking. The latter can pose a dramatic threat to the integrity of large pressure vessels welding joints and hence the equipment lifetime.</p>

The Influence of Low Melting Point Elements on Hot-Cracking of 310 Austenitic Stainless Steel

Paper Proceedings: https://asmedigitalcollection.asme.org/PVP/PVP2021/volume/85314

ASME 2021 Pressure Vessels & Piping Conference (PVP2021)

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.