<p class="MsoNormal">Internal hydrogen can influence the fatigue life, crack growth rate, and crack morphology of austenitic stainless steel, but little is known about the effect of internal hydrogen on fatigue crack initiation sites. To determine the effect of internal hydrogen on the microstructural fatigue crack initiation sites, the location of small fatigue cracks was evaluated with respect to the microstructural features in notched middle tension M(T) 316L specimens both with and without pre-charged hydrogen. The notches of the M(T) specimens were electropolished prior to fatigue testing to facilitate post-test analysis. Fatigue tests were performed with the same constant load amplitude and an R-ratio of 0.1 for specimens with and without internal hydrogen. The fatigue tests were interrupted after a minimal amount of cracking was detected using the direct current potential difference (DCPD) technique. The microstructural locations of the small fatigue cracks were then evaluated with scanning electron microscopy imaging and electron backscatter diffraction (EBSD). Several small transgranular fatigue cracks initiated in the notches of specimens both with and without internal hydrogen. These transgranular cracks intersected grain boundaries and did not follow the prominent slip traces. There was no discernible effect of hydrogen on the microstructural sites of fatigue crack initiation in 316L.</p>

Effect of Internal Hydrogen on Fatigue Crack Initiation Sites in 316L Austenitic Stainless Steel

Paper Proceedings: https://asmedigitalcollection.asme.org/PVP/PVP2021/volume/85314

ASME 2021 Pressure Vessels & Piping Conference (PVP2021)

Supporting the need among researchers worldwide for additional online and multimedia content, ASME now offers the ASME Conference Video Collection. This platform will collect and provide long-term access to conference presentation videos, encompassing all technology areas within ASME's technical conference and events program. About 30,000-40,000 engineers across all mechanical engineering and related disciplines participate in ASME conferences each year. This includes authors of approximately 6,000 to 8,000 technical papers published by ASME, the majority of whom also submit video presentations for our virtual conferences. The video collection will be available as an add-on to existing product packages or as a separate subscription.