Silicon (Si)-based materials have been considered as the most promising anode materials for high-energy-density lithium-ion batteries because of their higher storage capacity and similar operating voltage, as compared to the commercial graphite (Gr) anode. But the use of Si anodes including silicon-graphite (Si-Gr) blended anodes often leads to rapid capacity decay in Si-Gr/LiNixMnyCozO2 (x+y+z=1) full cells, which has been attributed to surface instability of the Si component. In addition to stabilizing the surface, this work investigates the capacity decay of the Si-Gr blended anodes in a full-cell configuration and the capacity contribution from both active components. Using dQ/dV plots of the full cells, a powerful but simple-to-implement differential potential approach is developed to decouple the capacity contribution and degradation from the graphite and silicon components. Data collected from three-electrode cells confirm the results from the differential potential approach, which suggests a voltage slippage to a higher voltage at the blended anode side. The voltage slippage causes a reduced utilization of the Gr component and exacerbates side reactions between the Si-Gr anode and carbonate electrolytes. Furthermore, based on these failure mechanisms, we adopted a mitigation strategy to tune the open circuit voltage of the prelithiated anode while stabilizing the surface.

Investigation of the rapid capcity decay in silicon-based full batteries

Fall 2022 abstracts, posters, and presentations will launch in mid-September.

ACS Fall 2022

The official archive and repository for all ACS Meetings & Expositions abstracts and select posters or presentations.